Main Business
-
-
-
PRODUCTS
Xintianhe Resin
Vinyl Resin
Product grade
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Vinyl
300-500
10-30
110
80
6
Bisphenol A type epoxy resin has excellent resistance to chemical corrosion, outstanding overall mechanical properties, low shrinkage, and good workability.
Vinyl
200-300
20-40
110
85
7
Higher solid content, better wettability and leveling properties, improved fatigue resistance and water resistance, and excellent bonding effect with the substrate.
Vinyl
150-250
20-40
110
79
5
Pre-promoted bisphenol A epoxy resin, low viscosity pre-promoted resin, is extremely suitable for vacuum infusion molding processes, while also possessing excellent glass fiber wetting effects and its own degassing effect. Compared to similar types of resins, TH-120P-1 has a higher solid content, better wettability, improved fatigue resistance and water resistance, and an extremely low volume shrinkage rate.
Vinyl
250-350
20-40
110
79
5
Higher solid content, better wettability, extremely low volume shrinkage, and good anti-sagging performance.
Vinyl
450-650
10-20
110
75
6
Better wettability, superior mechanical properties, and improved processability.
Vinyl
250-350
10-30
145
80
4
It can maintain good rigidity and strength at higher temperatures, while also exhibiting resistance to corrosion from acids, organic solvents, and acidic oxidative media. Especially in acidic oxidative environments, it has a long-term tolerance. Additionally, its construction operability is very good, making it suitable for various fiberglass molding processes. This is a high-temperature resistant fiberglass heavy anti-corrosion resin.
Vinyl
500-800
10-30
165
70
3
It can maintain good rigidity and strength at higher temperatures, while also having resistance to corrosion from acids, organic solvents, and acidic oxidative media. Especially in acidic oxidative environments, it has a long-term tolerance. Additionally, its construction operability is very good, making it suitable for various fiberglass molding processes. It is widely used in chemical engineering and industry involving numerous chemical media such as acids, bases, salts, and organic solvents. It is an ideal high-temperature resistant fiberglass heavy anti-corrosion resin.
Vinyl
250-350
10-20
100
70
4
Brominated epoxy resin suitable for meeting the dual requirements of high flame retardancy and high corrosion resistance, with ultra-high reactivity, is suitable for hand lay-up, winding, pultrusion, and other molding processes. It also has excellent glass fiber wetting effect and mechanical strength. Compared to similar types of resins, TH-310 exhibits excellent flame retardant effects, superior wettability, outstanding mechanical properties, and better processability. The oxygen index of pure resin castings can reach above 35.
Vinyl
250-350
10-30
100
65
4
It has excellent flame retardant effects and superior wettability, with a pure resin casting body oxygen index reaching above 33, making it suitable for the production of flame retardant light-transmitting panels and flame retardant compartment boards.
Vinyl
350-550
10-20
100
70
4
Suitable for hand lay-up, winding, vacuum infusion and other forming processes, it has excellent flame retardant effects, superior wettability, outstanding mechanical properties, and better processability. The oxygen index of pure resin castings can reach above 33, making it particularly suitable for the production of composite material photovoltaic frames, and it has obtained TÜV RHEINLAND certification.
Vinyl
1500-2200
110
77
7.5
18
It has excellent thickening effects, good mechanical strength, and resistance to chemical corrosion, making it suitable for molding processes such as SMC and BMC. It also features superior wettability, very low volume shrinkage, and good processability.
Vinyl
1800-2400
105
80
9
22
It has extremely high impact resistance and fatigue resistance, while also providing excellent thickening effects, making it suitable for molding processes such as SMC and BMC. It features higher impact resistance, superior wettability, very low volume shrinkage, and good processability.
Vinyl
1800-2400
110
80
8
30
It has extremely high impact resistance and fatigue resistance, while also providing excellent thickening effects, making it suitable for molding processes such as SMC and BMC. Compared to similar types of resins, TH-450-2 offers higher impact resistance, better wettability, very low volumetric shrinkage, and good processability.
Vinyl
300-500
10-20
110
70
10
25
It has excellent impact resistance and elongation at break, as well as good mechanical strength and fatigue resistance. Compared to similar types of resins, TH-480 exhibits outstanding impact resistance, superior mechanical properties, lower volumetric shrinkage, and good processability.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 800-820-8357 / 400-619-0529
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin