Xintianhe Resin
Solid surface materials resin
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Phthalate
600-800
3-5
55
45
4.0
5.0
Moderate viscosity, good wettability for fillers, high hardness, and high mechanical strength, specifically designed for artificial marble color particles.
Meta-phenylene NPG/MMA
800-1100
6-9
65
70
4.0
10.0
Isophorone new pentanediol modified composite acrylic resin. High-end sheets, basins, waistlines, bathrooms, etc. The products have excellent weather resistance, water resistance, and aging resistance.
M-Xylene/MMA
800-1100
5-9
67
65
3.0
8.0
Meta-phenylene modified composite acrylic resin, with high impact resistance and good filling performance and defoaming properties, used for making high-end artificial marble, countertops, etc.
Meta-phenylene NPG/MMA
800-1100
6-9
65
70
4.0
10.0
Isophorone new pentanediol modified composite acrylic resin. High-end sheets, washbasins, waistline bathroom products, etc. The products have excellent weather resistance, water resistance, and aging resistance.
Phthalate
500-700
3-5
55
60
8.0
12
The filler has good wettability, high transparency, and the products are not easy to crack, making it suitable for artificial marble, countertops, etc.
Phthalate
1400-2200
3-5
55
60
6.0
8.0
High adhesion and strong wettability. Suitable for artificial marble splicing and adhesive use, with a high cost-performance ratio.
Phthalate
400-550
3-5
58
50
6.0
8.0
The filler has good wettability, high transparency, and high toughness, making it suitable for the production of artificial marble, countertops, and more.
Phthalate
650-850
5-8
60
65
6.0
8.0
The filler has good wettability, high transparency, and high toughness, making it suitable for the manufacture of artificial marble, bathroom products, and more.
Phthalic acid/MMA
650-850
5-8
65
65
6.0
10.0
The filler has good wettability, high transparency, can be mixed with some methyl methacrylate, has good weather resistance, and high toughness, making it suitable for manufacturing artificial marble, countertops, and bathroom products.
Phthalate
650-900
5-8
60
65
6.0
9.0
High hardness, no post-curing treatment is required when making artificial marble slabs. It can also be used to make decorative pieces such as waistlines.
NPG/Phthalate
700-900
5-8
63
68
5.0
10.0
New pentaerythritol modified phthalic resin, high toughness, not easy to break, good weather resistance, used for artificial marble, transparent sheets, artificial agate, etc.
NPG/MMA
700-900
5-8
65
65
5.0
10.0
Benzene new pentanediol, composite acrylic resin, has good wettability, products are not easy to crack, suitable for making artificial marble, countertops, sanitary ware, etc.
Phthalate
650-850
6-9
67
65
3.0
3.0
Moderate viscosity, good wettability for fillers, high hardness, and high mechanical strength, specifically designed for artificial marble color particles.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin