Main Business
-
-
-
PRODUCTS
Xintianhe Resin
Thermosetting Resins
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
DCPD
400-600
9-12
8
12
DCPD-Modified Unsaturated Polyester Resin It has moderate viscosity and moderate reactivity, as well as excellent mechanical strength, electrical insulation properties and heat resistance. It is suitable for use as a resin for insulating varnishes..
DCPD
500-700
5-9
70
50
2
7.5
DCPD-Modified Unsaturated Polyester Resin It has moderate viscosity and moderate reactivity, as well as excellent mechanical strength, electrical insulation properties and heat resistance. It is suitable for use as a resin for insulating varnishes..
DCPD
400-600
6-8
70
50
2
5
Good fiberglass wettability, low styrene emission, high heat resistance, and good water resistance.
Double ring
600-1000
6-8
110
60
2.0
10.0
Pultrusion uses dual-ring resin, which has good wettability, high hardness, and relatively good gloss. It is suitable for various pultruded profiles.
DCPD
1300-1600
20-30
80
50
2.5
7.5
DCPD-Modified Unsaturated Polyester Resin This product features moderate viscosity and moderate reactivity, along with excellent toughness, high strength, good electrical insulation properties, and a high heat resistance temperature. When mixed with a high-temperature curing agent, it exhibits excellent storage stability. It is particularly suitable for single-component insulating varnishes..
DCPD/Orthophthalic type
250-500
7-9
75
55
2.5
6
Good fiberglass wettability, low styrene emission, high heat resistance, good chemical resistance.
DCPD
1300-1600
9-12
70
50
2
7.5
DCPD-Modified Unsaturated Polyester Resin It features moderate viscosity and moderate reactivity, along with high mechanical strength, good electrical insulation properties, and moderate heat resistance. It is particularly suitable for insulating varnish resins..
Double ring
650-850
2-5
75
50
3.5
Good storage stability, can cure quickly, suitable for resin used in marble glue.
DCPD
6000-8000
6-10
90
: DCPD-Modified Unsaturated Polyester Resin； Styrene-Free This resin exhibits moderate viscosity and moderate reactivity, along with excellent high-temperature curing performance, low volatility, good electrical insulation properties, and favorable heat resistance. It is suitable for insulating varnish resins that require low volatility
Phthalate
80-150
10-20
60
47
2.0
3.0
Pre-promoting, pre-thixotropic, with characteristics of low viscosity and fast post-curing speed. Good wettability to fillers, especially suitable for bonding between acrylic sheets, composite boards, and fiberglass, suitable for spraying processes.
Phthalate
600-900
4-8
70
60
6
15.0
The fiberglass has good wettability, fast pulling speed, and good brightness, making it suitable for extruded rod components such as spray gun rods and mosquito net rods, as well as profiles.
Phthalate
600-900
5-8
70
60
4.5
8.0
Good toughness, high strength, suitable for pulling and extruding rods and profiles.
Phthalate
550-950
4-8
75
70
3.0
10.0
With high mechanical strength and toughness, it is suitable for the extrusion process to manufacture mosquito net poles, tent poles, and various profiles with general requirements.
Phthalate
600-900
6-10
95
70
3.0
10.0
High activity, moderate viscosity, good wettability for glass fibers and fillers, widely applicable for the pultrusion process to manufacture mosquito net poles, tent poles, rods, sheets, and profiles. The pultruded fiberglass products have characteristics such as high mechanical strength, good toughness, excellent temperature resistance, and good surface brightness.
Orthophthalic type
200-300
11-13
70
65
3
10
Centrifugal cast pipes (HOBAS) structural layer resin, high tensile strength and elongation at break.
Orthophthalic type
300-400
5-7
-
10
40
Non-Break
Special resin for centrifugal casting (Hobas) lining layer , with extremely high toughness, high brightness and good air drying properties.
Orthophthalic type
300-500
2-6
80
65
3.0
10
Medium activity, moderate viscosity, fast post-curing, with high mechanical strength and toughness, suitable for various FRP pipes products by continuous winding process.
M-xylene
750-900
4-7
65
65
4.0
8.0
The isophthalic unsaturated polyester resin has excellent water resistance, stain resistance, and alkali resistance, making it suitable for products such as sanitary ware, decorative parts, and waistlines.
Metaxylene
350-550
8-12
65
70
3.0
6.0
Low viscosity, high strength, good alkali resistance, and excellent yellowing resistance. Good wettability with fillers. Used in automatic lines and artificial quartz stone products.
Meta-phenylene NPG/MMA
800-1100
6-9
65
70
4.0
10.0
Isophorone new pentanediol modified composite acrylic resin. High-end sheets, basins, waistlines, bathrooms, etc. The products have excellent weather resistance, water resistance, and aging resistance.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin