Product Description
DS-609PN (609N)
DS-Tianhe Resin Series
Tianhe Dianshi brand DS-609PN is a pre-accelerated (609N does not contain accelerators) isophthalic winding/pultrusion unsaturated polyester resin, with high reactivity, moderate viscosity, good wettability, good moisture and heat resistance, strong adaptability to downstream processes, good fatigue resistance, high circumferential load capacity, high mechanical strength, and high toughness. It is suitable for high-performance products in the fields of building materials, electrical, and civil use.
| Liquid Resin Technical Indicators | |||
| Item | Unit | Indicator | Testing Standard |
| Appearance | Light red transparent liquid | Visual | |
| Acid Value | mgKOH/g | 18-22 | GB2895 |
| Viscosity at 25℃ | mPa.S | 450-850 | GB7193 |
| Gel Time at 25℃ | min | 60-70 | GB7193 |
| Gel Time at 120℃ | min | 10-20 | |
| Solid Content | % | 62-65 | GB7193 |
| Stability at 80℃ | h | ≥24 | GB7193 |
| Note: 1) The gel time of 609PN at 25℃ in an air bath: Add 0.5ml MEKP (M-50) solution to 50g of resin. 2) The gel time of 609N (without accelerator) at 120℃ in an oil bath: Add 0.5g TBPB (Trigonox C) solution to 50g of resin. |
|||
| Resin Casting Body Performance Indicators (for reference only) | |||
| Item | Unit | Indicator | Testing Standard |
| Barcol Hardness | Barcol | 40 | GB3854 |
| Tensile Strength | MPa | 75 | GB2567 |
| Tensile Modulus | MPa | 3000 | GB2567 |
| Elongation at break | % | 3.0 | GB2567 |
| bending strength | MPa | 110 | GB2567 |
| bending modulus | MPa | 3000 | GB2567 |
| impact toughness | KJ/m² | 12 | GB2567 |
| heat distortion temperature | ℃ | 95 | GB1634.2 |
| Modulus of elasticity in circumferential bending | MPa | 3000 | |
| Elongation at break in circumferential bending | % | 2.2 | |
| Note: 1) Casting body sample preparation method: Follow GB/T8237-2005; 2) Post-processing method for casting body: Room temperature/24 hours +40℃/1 hour +60℃/3 hours; 3) Experimental environment temperature: 23±2℃, relative humidity: 50±5%. 4) Post-processing method for circumferential bending casting body:80℃/16h. |
|||
Packaging and Storage
(The packaging of Tianhe Dianshi brand DS-609PN (609N) is a net weight of 220KG metal drum, with a storage period of six months at a temperature of 20℃. Higher temperatures will shorten the storage period accordingly. It should be stored in a cool and ventilated place, avoiding direct sunlight and keeping away from heat sources. This product is flammable and should be kept away from open flames.)
(Note: This data is determined according to national standards (GB). Due to various factors affecting the processing process, the necessity for users to conduct their own experimental research cannot be excluded. Legally, it does not guarantee that certain performance of the product is completely applicable to a specific use and reserves the right to modify the information.)
: next page
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin