Main Business
-
-
-
PRODUCTS
Xintianhe Resin
Thermosetting Resins
Product grade
Categorization
Viscosity(mPa.s25℃)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Fracture elongation(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Fracture elongation(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Fracture elongation(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Carrier resin
3900-4100
The pigment carrier resin without styrene has a high viscosity, good compatibility, is suitable for grinding color powders, and has good color stability.
Phthalate
400-800
3-5
55
50
4.0
6.5
General transparent craft resin.
Phthalate
350-600
3-5
65
60
2.0
7.0
Good resistance to yellowing, high transparency, used for transparent crystal crafts.
Phthalate
350-600
3-5
65
60
2.0
7.0
Good resistance to yellowing, high transparency, used for making transparent flat panel crafts.
Double ring
120-220
9-14
20
15
The product has outstanding high-temperature performance at 200℃. It is easy to sand and easy to apply, making it suitable for use as a putty for powder coating on entire vehicles.
Specialty materials
150-300
9-14
22
17
Easy to sand, easy to apply, good high-temperature resistance, suitable for use as body putty.
Special modification
150-300
9-14
30
20
Good toughness, easy to polish, easy to apply and scrape, with good high-temperature resistance, suitable for making putty for the whole vehicle.
orthophthalic
600~800
5~7
60
60
10.0
12.0
With medium viscosity and medium reactivity, good toughness, excellent mechanical strength, good adhesive properties, good wetting properties and other characteristics. Especially used in natural marble crushed material bonding molding, products with good surface luminosity, good hardness.
orthophthalic
600~800
5~7
58
60
8.0
10.0
orthophthalic Styrene-free unsaturated polyester resin With medium viscosity and medium reactivity, good toughness, excellent mechanical strength, good bonding properties, good wetting properties and other characteristics. It is especially used for bonding and molding of natural marble crushed materials, with good surface brightness and good hardness.
Reactive
180-300
12-20
70
50
3.0
6
Reactive flame retardant, with an oxygen index of no less than 30, good resistance to yellowing, suitable for transparent corrugated sheets or flat panels.
Modification
150-250
8-20
60
42
2.0
3.0
Excellent fiberglass wetting ability, with strong adhesion to acrylic sheets and ABS composite boards.
Modification
150-250
8-20
60
42
2.0
3.0
It has excellent adhesion to acrylic and composite boards.
Phthalate
90-200
8-25
60
60
2.0
5.0
Low viscosity, fast curing, excellent fiberglass wetting ability, and strong adhesion to acrylic sheets.
Phthalate
300-500
10-30
75
65
3.0
6.0
Strong adhesion, good air-drying properties, fast curing, suitable for fiberglass wrapping on the surface of natural marble stone to prevent cracking during cutting.
Reactive
120-200
25-35
75
50
3.0
6.0
Reactive flame retardant, with an oxygen index of not less than 30, suitable for RTM or vacuum infusion molding processes to produce helmets, battery covers for new energy vehicles, and other fiberglass products with flame retardant requirements.
Reactive
180-300
5-9
75
50
5.0
10
Reactive flame retardant, with an oxygen index of not less than 26, suitable for corrugated or flat panels with certain flame retardant requirements.
Reactive
300-500
5-9
70
50
3.0
7
Reactive flame retardant, with an oxygen index not less than 32, suitable for hand lay-up, winding, pultrusion, and other molding processes.
Reactive
220-280
30-54
70
50
3.0
7
Reactive flame retardant, pre-promoting resin, with an oxygen index not less than 32, suitable for hand lay-up and spray molding.
Reactive
180-300
5-9
73
50
5.0
7
Reactive flame retardant, with an oxygen index not less than 30, suitable for corrugated or flat panels with higher flame retardant requirements.
Polyurethane modification
400-600
8-12
35
20
100
110
Polyurethane-modified resin features high elongation, excellent flexibility, and relatively high strength. It can be added to other resins to enhance their fracture resistance, elongation at break, and impact performance. Additionally, it can be used alone to produce impact-resistant products and flexible products..
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin