Xintianhe Resin
Thermosetting Resins
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Application
Categorization
Viscosity(mPa.s25℃)
Application
Categorization
Viscosity(mPa.s25℃)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Phthalate
500-600
20-30
55
45
15
20
Moderate hardness, excellent impact resistance, suitable for billiards.
Carrier resin
2500-3500
Color powder carrier resin without active monomers such as styrene has moderate viscosity, good compatibility, and excellent coloring properties. This carrier can copolymerize with unsaturated polyester resin, having minimal impact on curing.
Orthophthalic
200-300
10-15
70
60
3.0
10
Good wettability, good air-drying, high toughness, low shrinkage, application for the machining FRP sheets.
Orthophthalic
180-300
25-35
70
60
3.0
7
Pre-accelerated resin, good process adaptability, low curing shrinkage, high toughness, good mechanical strength, application to machining FRP sheets.
Phthalate
220-280
30-54
70
60
3.0
5
Pre-cured resin, with high mechanical strength, is suitable for the manufacturing of vehicle body components.
Phthalate
180-300
5-9
70
70
3.0
7
Pre-promoted resin, high flatness of the board, high mechanical strength, used for machine-made FRP flat panels.
orthophthalic
300-500
30-36
75
60
4.0
5
orthophthalic unsaturated polyester resin of pre-accelerated type made with the addition of imported silicon dioxide and other thixotropy agent. The resin has good water resistance and high mechanical properties, no sagging over the verticals, particularly applicable for manufacturing of marine and cooling tower..
orthophthalic
300-500
30-36
75
60
4.0
5
unsaturated polyester resin of pre-thixotropic type made with the addition of imported silicon dioxide and other thixotropy agent. The resin has good water resistance and high mechanical properties, no sagging over the verticals, particularly applicable for manufacturing of marine and cooling tower.
orthophthalic
400-500
5-9
75
65
2.2
10.0
orthophthalic unsaturated polyester resin of pre-accelerated and thixotropic type made with the addition of imported silicon dioxide and other thixotropy agent. The resin has good water resistance and high mechanical properties, no sagging over the verticals, particularly applicable for manufacturing of auto parts,marine and cooling tower..
Bisphenol A
200-300
5-9
75
55
4
6
Good corrosion resistance, high heat resistance, suitable for use in high-demand areas such as tank linings and flooring.
Modified
180-300
12-20
65
55
5.0
10
Pre-promoted resin, high flatness of the board, good toughness, excellent overall performance, used for mechanized FRP flat panels.
Double ring
280-460
25-45
80
50
2.5
5
Low volatility, good wettability of glass fiber, suitable for manufacturing air conditioning covers and other products.
Carrier resin
400-600
Magnesium oxide powder special carrier resin without styrene. Moderate viscosity, good compatibility, magnesium oxide powder is evenly dispersed and not easy to settle, with stable storage.
Carrier resin
800-1000
The color powder special carrier resin without styrene has moderate viscosity, good compatibility, high color powder filling capacity, and extremely stable color, making it suitable for coloring molded products.
Carrier resin
400-600
Styrene-free color powder special carrier resin, with moderate viscosity, good compatibility, high color powder filling capacity, and extremely stable color, suitable for coloring products made by processes such as molding of fiberglass.
DCPD
200-350
10-30
65
55
2.5
7
DCPD modified unsaturated polyester resin features low viscosity, good leveling property, excellent air-drying performance, low shrinkage rate of products, and strong adhesion to epoxy resin. It is suitable for manufacturing corrosion-resistant floors with epoxy resin.
Double ring
80-150
3-10
67
52
2.6
5.8
Low viscosity, good wetting ability of glass fiber, suitable for enhancing the back of products such as acrylic and composite board bathtubs.
Double ring
200-400
3-10
70
60
3.0
6.0
Excellent fiberglass wetting ability, suitable for enhancing the back of products such as acrylic and composite board bathtubs.
Double ring
150-350
2-6
70
55
4.0
7.0
Medium viscosity and medium reactivity, fast curing after setting, crack-resistant, good toughness, suitable for basin casting, resin-based concrete casting and other products.
M-xylene / neopentyl glycol
400-1000 seasonally adjusted
Seasonally adjusted 4-10
100
65
2.0
9.0
The viscosity is suitable, and it has good wettability for fiberglass fabrics. It meets the thickening requirements of prepregs at different ambient temperatures, resulting in a long storage period for the prepreg, low volatility of styrene odor, and easy application to pipe walls in various temperature environments. The cured product has high mechanical strength, good toughness, heat resistance, water resistance, corrosion resistance, and excellent weather resistance, making it suitable for CIPP UV curing and CIPP hot water inversion method for repairing pipe liners.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin