Xintianhe Resin
Unsaturated Polyester Resin
Pultrusion
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
M-xylene
600-1000
5-10
85
70
2.8
6.0
High strength, good process performance, good surface quality, suitable for profiles such as photovoltaic brackets.
Metaxylene
900-1300
5-10
80
70
3.2
8.0
High strength, good processability, good surface quality, high gloss, suitable for extrusion profiles.
Metaxylene
600-900
5-10
85
70
3.3
6.0
Fast pulling speed, good surface quality, high gloss, good processing performance, suitable for extrusion profiles.
M-xylene
600-900
3-10
90
70
3.3
12.0
Fast pulling speed, good surface quality, high gloss, good process performance, suitable for extruded profiles.
M-xylene
420-680
9-15
78
70
3.0
7.0
Good fiberglass wetting properties, high mechanical strength and heat resistance, suitable for rods and profiles.
Phthalate
600-900
3-5
70
65
6
9.0
Moderate reactivity, good surface brightness, high mechanical strength, suitable for solid rods and thicker profiles.
Phthalate
600-900
9-15
75
65
3.0
4.0
High strength, good toughness, high heat distortion temperature, suitable for rods and profiles.
Phthalate
600-900
5-9
75
65
3.0
4.0
High reactivity, high strength, good surface quality, suitable for pulling pipes and profiles.
Phthalate
600-900
5-8
80
65
4
10.0
High reactivity, good surface brightness, high mechanical strength, suitable for antenna covers, thin-walled rods, or online woven pull-wound tubes.
Benzene
600-900
5-10
95
65
3.1
6.0
Fast pulling speed, good surface quality, high gloss, good processing performance, suitable for medium to high-end extruded profiles.
Double ring
600-1000
6-8
110
60
2.0
10.0
Pultrusion uses dual-ring resin, which has good wettability, high hardness, and relatively good gloss. It is suitable for various pultruded profiles.
Phthalate
600-900
4-8
70
60
6
15.0
The fiberglass has good wettability, fast pulling speed, and good brightness, making it suitable for extruded rod components such as spray gun rods and mosquito net rods, as well as profiles.
Phthalate
600-900
5-8
70
60
4.5
8.0
Good toughness, high strength, suitable for pulling and extruding rods and profiles.
Phthalate
550-950
4-8
75
70
3.0
10.0
With high mechanical strength and toughness, it is suitable for the extrusion process to manufacture mosquito net poles, tent poles, and various profiles with general requirements.
Phthalate
600-900
6-10
95
70
3.0
10.0
High activity, moderate viscosity, good wettability for glass fibers and fillers, widely applicable for the pultrusion process to manufacture mosquito net poles, tent poles, rods, sheets, and profiles. The pultruded fiberglass products have characteristics such as high mechanical strength, good toughness, excellent temperature resistance, and good surface brightness.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin