Main Business
-
-
-
PRODUCTS
Xintianhe Resin
Unsaturated Polyester Resin
Molded (SMC BMC) resin
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Meta-xylene / Neopentyl glycol type
1400-1600
5-7
130
65
2.5
8
SMC/BMC resin, thickening and stabilizing, high surface gloss, excellent electrical properties, water resistance, and corrosion resistance, with low shrinkage. Suitable for molded products with high performance requirements.
Metaphenylene
1300-1500
9-11
120
65
2.5
8
SMC/BMC resin, thickening stability, high mechanical strength, good electrical properties, weather resistance, and corrosion resistance. Suitable for structural components with high strength requirements.
Benzene type
1300-1500
9-11
125
65
4.5
10
SMC/BMC dedicated resin, thickening stability, high gloss, high tensile strength, good impact toughness. Suitable for various ordinary molded products.
Phthalic type
1400-1600
8-10
120
65
2.5
10
SMC/BMC resin has high versatility, with slow thickening in the early stage and fast thickening in the later stage. It has high mechanical strength, good electrical performance, and relatively good gloss. It is suitable for various structural components.
Phthalic type
1400-1600
7-9
115
65
2.5
10
SMC/BMC resin, thickening and stabilizing, with high gloss and good toughness. Suitable for making large volume molded products.
Phthalic type
1400-1600
10-12
110
65
4.0
10
SMC/BMC resin, thickening and stabilizing, high cost-performance ratio, high mechanical strength, and very good toughness. Suitable for making large area molded products for surface painting.
Phthalic type
1300-1700
8-12
130
65
2.5
12
High reactivity, thickening stability, with advantages such as high gloss, high heat resistance, and high toughness. Widely applicable to the fields of automotive pressing, rail transportation, electrical components, construction facilities, and industrial and civilian equipment where there are high requirements for mechanical strength, electrical performance, toughness, glossiness, and shrinkage control in molded products.
Double ring
1000-1400
7-9
125
60
2.0
10
SMC/BMC uses dual-ring resin, which is thickened and stable, has good wettability, high hardness, and relatively good gloss. It is suitable for various molded structural parts.
Phthalic type
1100-1300
7-9
130
65
3.0
10
SMC/BMC resin, thickening stability, high gloss, high strength, good toughness. Suitable for making various molded products.
Phthalic type
1400-1600
5-7
130
65
2.5
10
SMC/BMC resin, thickening stability, high mechanical strength, good toughness, high gloss, and low shrinkage rate. Suitable for making various high-performance structural molded products.
Phthalic type
600-800
5-7
140
55
2.0
7
SMC special resin, low viscosity, thickening stability, high gloss, good boiling water resistance and weather resistance. Suitable for making compression molded products with high brightness, high flatness, and high temperature resistance.
High activity
2500-2700
7-9
140
55
2.5
8
SMC/BMC resin, high viscosity, thickening stability, high reactivity, relatively high toughness, and high heat resistance. Suitable for making compression molded products with high brightness and high temperature resistance.
High activity
1800-2000
9-11
140
55
2.0
7
SMC/BMC resin, high viscosity, thickening stability, high reactivity, and good heat resistance. Suitable for molded products with A-level surface requirements.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin