Xintianhe Resin
Unsaturated Polyester Resin
Hand lay-up resin
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Phthalate
110-180
9-15
68
60
3
7
Good permeability and transparency, suitable for the molding of fiberglass and carbon fiber.
Double ring
400-600
6-8
72
50
2.5
6
General-purpose resin, good air-drying properties, fast curing speed, and high mechanical strength.
Double ring
400-600
3-10
70
65
3
6
General-purpose resin with excellent mechanical properties and certain corrosion resistance.
Phthalate
380-620
5-9
73
60
3
8.5
General-purpose resin with excellent glass fiber wetting properties and mechanical strength.
Phthalate
225-375
5-9
75
60
3.5
8.5
General-purpose resin with excellent fiberglass wetting properties and mechanical strength.
Phthalate
300-500
15-30
70
60
3.5
8
Pre-promoted resin with excellent fiberglass wetting properties and mechanical strength, quick curing and demolding, suitable for automotive parts, tank heads, etc.
BPA (Bisphenol A)
450-650
5-15
76
55
4.0
6
Good corrosion resistance, high heat resistance, suitable for high-demand areas such as storage tank inner dimensions and flooring.
Phthalate
220-280
30-54
70
60
3.0
5
Pre-cured resin, with high mechanical strength, is suitable for the manufacturing of vehicle body components.
orthophthalic
300-500
30-36
75
60
4.0
5
orthophthalic unsaturated polyester resin of pre-accelerated type made with the addition of imported silicon dioxide and other thixotropy agent. The resin has good water resistance and high mechanical properties, no sagging over the verticals, particularly applicable for manufacturing of marine and cooling tower..
orthophthalic
300-500
30-36
75
60
4.0
5
unsaturated polyester resin of pre-thixotropic type made with the addition of imported silicon dioxide and other thixotropy agent. The resin has good water resistance and high mechanical properties, no sagging over the verticals, particularly applicable for manufacturing of marine and cooling tower.
Bisphenol A
200-300
5-9
75
55
4
6
Good corrosion resistance, high heat resistance, suitable for use in high-demand areas such as tank linings and flooring.
Double ring
280-460
25-45
80
50
2.5
5
Low volatility, good wettability of glass fiber, suitable for manufacturing air conditioning covers and other products.
M-xylene
400-600
5-9
85
70
5.0
7
Fast curing and demolding, good heat resistance, high mechanical strength, and good corrosion resistance.
orthophthalic
400-600
15-25
45
68
2.5
65
orthophthalic unsaturated polyester resin pre-accelerated and thixotropic. It has good wettability, no sagging on vertical surfaces, fast curing speed, low exotherm temperature, low shrinkage, and high mechanical strength, making it suitable for hand lay-up or spray up processes to manufacture thicker fiberglass products such as automotive parts and engine covers.
DCPD
300-500
20-40
80
55
3.0
5
DCPD pre-accelerated and thixotropic type unsaturated polyester resin,Good water resistance, high mechanical strength, no vertical hanging, low volatilization, especially suitable for auto parts, cooling tower and other products
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin