Unsaturated Polyester Resin
Reinforced Resin
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Application
Categorization
Viscosity(mPa.s25℃)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Phthalate
90-200
8-25
60
60
2.0
5.0
Low viscosity, fast curing, and excellent wetting ability of fiberglass on acrylic sheets.
Phthalate
80-150
10-20
60
50
2.0
3.0
The characteristics of pre-promoting, pre-thixotropic, low viscosity, and fast post-curing speed provide good wettability for fiberglass, making it particularly suitable for bonding between acrylic sheets, composite boards, and fiberglass.
Double ring
400-600
3-10
70
65
3
6
General-purpose resin with excellent mechanical properties and certain corrosion resistance.
Phthalate
120-200
60-90
80
60
3.0
3.0
Good fluidity, good permeability, long applicability period, high strength, and small shrinkage deformation make it suitable for vacuum infusion processes to produce radar domes and other products.
Phthalate
120-200
16-22
70
70
3.0
10.0
Good infiltration, low exothermic peak, small curing shrinkage, good color, high mechanical strength, suitable for RTM molding process to produce automotive parts and other fiberglass products.
Phthalate
380-620
5-9
73
60
3
8.5
General-purpose resin with excellent glass fiber wetting properties and mechanical strength.
Phthalate
225-375
5-9
75
60
3.5
8.5
General-purpose resin with excellent fiberglass wetting properties and mechanical strength.
Phthalate
100-300
5-9
70
65
3.0
7
Good permeability and transparency, high brightness, excellent strength.
Phthalate
300-500
15-30
70
60
3.5
8
Pre-promoted resin with excellent fiberglass wetting properties and mechanical strength, quick curing and demolding, suitable for automotive parts, tank heads, etc.
BPA (Bisphenol A)
450-650
5-15
76
55
4.0
6
Good corrosion resistance, high heat resistance, suitable for high-demand areas such as storage tank inner dimensions and flooring.
Phthalate
420-700
6-10
85
60
2.5
8.0
Excellent mechanical strength and heat resistance, with minimal deformation.
Carrier resin
3500-4000
Non-styrene carrier resin. It has a high viscosity, high grinding shear force, uniform dispersion of color powder, not easy to settle, and high storage stability.
Carrier resin
3900-4100
The pigment carrier resin without styrene has a high viscosity, good compatibility, is suitable for grinding color powders, and has good color stability.
Reactive
180-300
12-20
70
50
3.0
6
Reactive flame retardant, with an oxygen index of no less than 30, good resistance to yellowing, suitable for transparent corrugated sheets or flat panels.
Modification
150-250
8-20
60
42
2.0
3.0
Excellent fiberglass wetting ability, with strong adhesion to acrylic sheets and ABS composite boards.
Modification
150-250
8-20
60
42
2.0
3.0
It has excellent adhesion to acrylic and composite boards.
Phthalate
90-200
8-25
60
60
2.0
5.0
Low viscosity, fast curing, excellent fiberglass wetting ability, and strong adhesion to acrylic sheets.
Phthalate
300-500
10-30
75
65
3.0
6.0
Strong adhesion, good air-drying properties, fast curing, suitable for fiberglass wrapping on the surface of natural marble stone to prevent cracking during cutting.
Reactive
120-200
25-35
75
50
3.0
6.0
Reactive flame retardant, with an oxygen index of not less than 30, suitable for RTM or vacuum infusion molding processes to produce helmets, battery covers for new energy vehicles, and other fiberglass products with flame retardant requirements.
Reactive
180-300
5-9
75
50
5.0
10
Reactive flame retardant, with an oxygen index of not less than 26, suitable for corrugated or flat panels with certain flame retardant requirements.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin