Main Business
-
-
-
PRODUCTS
Xintianhe Resin
Unsaturated Polyester Resin
Reinforced Resin
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
DCPD
400-600
6-8
70
50
2
5
Good fiberglass wettability, low styrene emission, high heat resistance, and good water resistance.
Double ring
600-1000
6-8
110
60
2.0
10.0
Pultrusion uses dual-ring resin, which has good wettability, high hardness, and relatively good gloss. It is suitable for various pultruded profiles.
DCPD/Orthophthalic type
250-500
7-9
75
55
2.5
6
Good fiberglass wettability, low styrene emission, high heat resistance, good chemical resistance.
Phthalate
80-150
10-20
60
47
2.0
3.0
Pre-promoting, pre-thixotropic, with characteristics of low viscosity and fast post-curing speed. Good wettability to fillers, especially suitable for bonding between acrylic sheets, composite boards, and fiberglass, suitable for spraying processes.
Phthalate
600-900
4-8
70
60
6
15.0
The fiberglass has good wettability, fast pulling speed, and good brightness, making it suitable for extruded rod components such as spray gun rods and mosquito net rods, as well as profiles.
Phthalate
600-900
5-8
70
60
4.5
8.0
Good toughness, high strength, suitable for pulling and extruding rods and profiles.
Phthalate
550-950
4-8
75
70
3.0
10.0
With high mechanical strength and toughness, it is suitable for the extrusion process to manufacture mosquito net poles, tent poles, and various profiles with general requirements.
Phthalate
600-900
6-10
95
70
3.0
10.0
High activity, moderate viscosity, good wettability for glass fibers and fillers, widely applicable for the pultrusion process to manufacture mosquito net poles, tent poles, rods, sheets, and profiles. The pultruded fiberglass products have characteristics such as high mechanical strength, good toughness, excellent temperature resistance, and good surface brightness.
Orthophthalic type
200-300
11-13
70
65
3
10
Centrifugal cast pipes (HOBAS) structural layer resin, high tensile strength and elongation at break.
Orthophthalic type
300-400
5-7
-
10
40
Non-Break
Special resin for centrifugal casting (Hobas) lining layer , with extremely high toughness, high brightness and good air drying properties.
Orthophthalic type
300-500
2-6
80
65
3.0
10
Medium activity, moderate viscosity, fast post-curing, with high mechanical strength and toughness, suitable for various FRP pipes products by continuous winding process.
Terephthalic
150-350
10-20
75
65
2.5
8
Low viscosity and low reactivity. It is crack-resistant, good toughness, suitable for resin-based concrete casting products.
DCPD
200-400
10-15
75
55
2.0
6.5
Low viscosity and low reactivity. It is crack-resistant, has good toughness, suitable for resin-based concrete casting products.
Phthalate / Neopentyl Glycol Type
2200-3100
7-9
130
60
2.0
8
BMC special resin, with high reactivity, good fluidity, high gloss, high molding temperature, long storage period for material lumps, suitable for molding resin of electrical components.
Meta-xylene / Neopentyl glycol type
2100-2300
6-8
120
65
2.5
8
BMC special resin has a high surface gloss, excellent electrical properties, water resistance, and corrosion resistance. It is suitable for molded products with high performance requirements.
Meta-xylene / Neopentyl glycol type
1400-1600
5-7
130
65
2.5
8
SMC/BMC resin, thickening and stabilizing, high surface gloss, excellent electrical properties, water resistance, and corrosion resistance, with low shrinkage. Suitable for molded products with high performance requirements.
Metaphenylene
1300-1500
9-11
120
65
2.5
8
SMC/BMC resin, thickening stability, high mechanical strength, good electrical properties, weather resistance, and corrosion resistance. Suitable for structural components with high strength requirements.
Benzene type
1300-1500
9-11
125
65
4.5
10
SMC/BMC dedicated resin, thickening stability, high gloss, high tensile strength, good impact toughness. Suitable for various ordinary molded products.
Phthalic type
1400-1600
6-8
110
65
3.0
8
BMC special resin has high elongation at break and good impact toughness. It is suitable for various structural components.
Benzene type
2100-2300
7-9
130
60
2.5
8
BMC special resin, high cost-performance ratio, good weather resistance, high gloss, and low shrinkage rate. Suitable for various high-demand molded products.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin