Main Business
-
-
-
PRODUCTS
Xintianhe Resin
Unsaturated Polyester Resin
Reinforced Resin
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Solid content(%)
Application
Categorization
Viscosity(mPa.s25℃)
Solid content(%)
Application
Categorization
Viscosity(mPa.s25℃)
Solid content(%)
Application
Cresol type
2100-2300
6-8
110
60
5.0
10
BMC special resin, low cost, good coloring ability, high elongation at break, and good impact toughness. Suitable for products such as manhole covers and water pipes.
Cresol type
2100-2300
6-8
110
60
5.0
10
BMC special resin, low cost, good coloring ability, high elongation at break, and good impact toughness. Suitable for molded products such as manhole covers and water tanks.
Phthalic type
1400-1600
8-10
120
65
2.5
10
SMC/BMC resin has high versatility, with slow thickening in the early stage and fast thickening in the later stage. It has high mechanical strength, good electrical performance, and relatively good gloss. It is suitable for various structural components.
Phthalic type
1400-1600
7-9
115
65
2.5
10
SMC/BMC resin, thickening and stabilizing, with high gloss and good toughness. Suitable for making large volume molded products.
Phthalic type
1400-1600
10-12
110
65
4.0
10
SMC/BMC resin, thickening and stabilizing, high cost-performance ratio, high mechanical strength, and very good toughness. Suitable for making large area molded products for surface painting.
Phthalic type
1300-1700
8-12
130
65
2.5
12
High reactivity, thickening stability, with advantages such as high gloss, high heat resistance, and high toughness. Widely applicable to the fields of automotive pressing, rail transportation, electrical components, construction facilities, and industrial and civilian equipment where there are high requirements for mechanical strength, electrical performance, toughness, glossiness, and shrinkage control in molded products.
Double ring
1000-1400
7-9
125
60
2.0
10
SMC/BMC uses dual-ring resin, which is thickened and stable, has good wettability, high hardness, and relatively good gloss. It is suitable for various molded structural parts.
Maleic type
2500-2700
10-12
210
50
2.0
7
It has characteristics such as high heat distortion temperature, resistance to boiling water, good high-temperature resistance, and excellent corrosion resistance. It has good wettability with fillers and glass fibers. It is suitable for wide addition to various molding process resins such as hand lay-up, winding, casting, pultrusion, and RTM, significantly improving the product's heat distortion temperature, high-temperature resistance, boiling water resistance, and corrosion resistance.
Phthalic type
1100-1300
7-9
130
65
3.0
10
SMC/BMC resin, thickening stability, high gloss, high strength, good toughness. Suitable for making various molded products.
Phthalic type
1400-1600
5-7
130
65
2.5
10
SMC/BMC resin, thickening stability, high mechanical strength, good toughness, high gloss, and low shrinkage rate. Suitable for making various high-performance structural molded products.
Phthalic type
600-800
5-7
140
55
2.0
7
SMC special resin, low viscosity, thickening stability, high gloss, good boiling water resistance and weather resistance. Suitable for making compression molded products with high brightness, high flatness, and high temperature resistance.
High activity
2500-2700
7-9
140
55
2.5
8
SMC/BMC resin, high viscosity, thickening stability, high reactivity, relatively high toughness, and high heat resistance. Suitable for making compression molded products with high brightness and high temperature resistance.
High activity
1800-2000
9-11
140
55
2.0
7
SMC/BMC resin, high viscosity, thickening stability, high reactivity, and good heat resistance. Suitable for molded products with A-level surface requirements.
orthophthalic
500-900
8-15
70
55
4.0
7.5
orthophthalic type unsaturated polyester resin, It has medium viscosity and high reactivity. High strength, good toughness, not easy to crack, excellent wear resistance, fast curing, suitable for making crystal millstone products.
orthophthalic
80-160
3-8
75
65
2.3
5.0
promoted orthophthalic unsaturated polyester resin have low viscosity and moderate reactivity. They boast high strength, good toughness and are not easy to crack, with fast post-curing, easy demolding and excellent air-drying performance. They are applied to polished abrasive products.
orthophthalic
400-600
15-25
45
68
2.5
65
orthophthalic unsaturated polyester resin pre-accelerated and thixotropic. It has good wettability, no sagging on vertical surfaces, fast curing speed, low exotherm temperature, low shrinkage, and high mechanical strength, making it suitable for hand lay-up or spray up processes to manufacture thicker fiberglass products such as automotive parts and engine covers.
DCPD
300-500
20-40
80
55
3.0
5
DCPD pre-accelerated and thixotropic type unsaturated polyester resin,Good water resistance, high mechanical strength, no vertical hanging, low volatilization, especially suitable for auto parts, cooling tower and other products
Polystyrene type
24000-26000
38-42
SMC/BMC dedicated low shrinkage additive, good coloring ability, good toughness, high gloss, and high mechanical strength.
Polystyrene type
18000-20000
38-42
SMC/BMC dedicated low shrinkage additive, with lower viscosity, good coloring ability, high gloss, and higher mechanical strength.
Saturated polyester type
200-300
46-50
SMC/BMC dedicated low-profile additives, high cost-performance ratio, good compatibility, excellent thickening ability, good coloring properties, low shrinkage rate, high surface hardness, and good gloss. Low viscosity can increase filling amount and reduce the cost of molded products.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin