Main Business
-
-
-
PRODUCTS
Xintianhe Resin
Unsaturated Polyester Resin
Non-reinforced resin
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Phthalate
400-550
3-5
58
50
6.0
8.0
The filler has good wettability, high transparency, and high toughness, making it suitable for the production of artificial marble, countertops, and more.
Phthalate
700-1100
10-13
67
70
5.0
10.0
Good wettability with fillers, high strength, and high degree of curing, used for artificial quartz stone products, especially dark-colored products.
Phthalate
350-550
10-13
63
65
5.0
10.0
Benzene-free styrene environmental products have good wettability with fillers and high strength, used for artificial quartz stone products.
Phthalate
650-850
5-8
60
65
6.0
8.0
The filler has good wettability, high transparency, and high toughness, making it suitable for the manufacture of artificial marble, bathroom products, and more.
Phthalic acid/MMA
650-850
5-8
65
65
6.0
10.0
The filler has good wettability, high transparency, can be mixed with some methyl methacrylate, has good weather resistance, and high toughness, making it suitable for manufacturing artificial marble, countertops, and bathroom products.
Phthalate
650-900
5-8
60
65
6.0
9.0
High hardness, no post-curing treatment is required when making artificial marble slabs. It can also be used to make decorative pieces such as waistlines.
Phthalate
400-600
4-7
60
65
5.0
7.0
The filler has good wettability, high transparency, and high toughness, making it suitable for decorative materials such as waistlines.
NPG/Phthalate
700-900
5-8
63
68
5.0
10.0
New pentaerythritol modified phthalic resin, high toughness, not easy to break, good weather resistance, used for artificial marble, transparent sheets, artificial agate, etc.
NPG/MMA
700-900
5-8
65
65
5.0
10.0
Benzene new pentanediol, composite acrylic resin, has good wettability, products are not easy to crack, suitable for making artificial marble, countertops, sanitary ware, etc.
Phthalate
300-550
3-5
60
65
7.0
10.0
High transparency, good filling performance and defoaming properties, used for making artificial marble, artificial agate, and bathroom products.
Phthalate
600-800
4-7
60
55
7.0
9.0
Good filling performance and defoaming properties, used for making artificial marble, sinks, and bathroom products.
Phthalate
400-600
4-7
65
67
3.0
5.0
Good filling performance and defoaming properties, used for making artificial marble, sinks, artificial agate, and bathroom products.
Phthalate
400-600
4-7
65
60
3.0
8.0
High transparency, good filling performance and defoaming ability, and excellent aging resistance. Used for making artificial marble, sinks, artificial agate, and bathroom products as well as their surface layers.
Phthalate
400-600
4-7
65
70
6.0
12.0
Good toughness, excellent filling performance and defoaming ability, used for making artificial marble, sinks, artificial agate, and bathroom products.
Phthalate
400-600
4-7
65
67
3.0
5.0
Good filling performance and defoaming ability, with excellent aging resistance. Used for making artificial marble, sinks, artificial agate, and bathroom products as well as their surface layers.
Phthalate
350-550
8-12
63
65
3.0
6.0
Low viscosity, high strength, good resistance to yellowing. Good wettability with fillers. Used in automatic lines and artificial quartz stone products.
DCPD
900-1200
3-6
75
50
3.5
8.5
Unsaturated Polyester Resin Specialized for Anchoring Agents This product is a modified version of conventional unsaturated polyester resin. It features high reactivity, short gel time, fast curing speed, long storage life, and high strength. Compared with conventional unsaturated polyester resin, it can reduce the consumption of accelerators and curing agents, simplify production processes, lower production costs, and facilitate operation
DCPD
900-1400
2-4
75
50
3.5
8.5
Unsaturated Polyester Resin Specialized for Anchoring Agents, pre-accelerated This product is a modified form of conventional unsaturated polyester. It exhibits high reactivity, short gel time, fast curing speed, long storage life, and high strength. Compared with conventional unsaturated polyester resin, it can reduce the consumption of accelerators and curing agents, simplify production processes, lower production costs, and facilitate operation..
Phthalate
650-850
6-9
67
65
3.0
3.0
Moderate viscosity, good wettability for fillers, high hardness, and high mechanical strength, specifically designed for artificial marble color particles.
Orthophthalic
650-950
2-6
65
70
3.0
11.0
Has a low viscosity, high reactivity and high hardness, the main application areas for the surface coating, with good leveling, good adhesion, surface drying better characteristics, the actual application is good surface flatness.
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin