Xintianhe Resin
Unsaturated Polyester Resin
Non-reinforced resin
Product grade
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Fracture elongation(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Fracture elongation(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s25℃)
Gel time(min)
Fracture elongation(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Categorization
Viscosity(mPa.s 25℃)
Gel time(min)
Heat distortion temperature(℃)
Tensile strength(MPa)
Elongation at break(%)
Impact toughness(KJ/㎡)
Application
Double ring
150-300
4-6
60
50
5.0
6.0
Good wettability with the filler, fast curing, and low shrinkage, used for making gel coat artificial stone basins.
Phthalate
600-800
3-5
55
45
4.0
5.0
Moderate viscosity, good wettability for fillers, high hardness, and high mechanical strength, specifically designed for artificial marble color particles.
ISO
600~800
5~7
63
65
10.0
10.0
It has medium viscosity and high reactivity, high strength, good toughness, excellent mechanical strength, good bonding performance, good dirt resistance and other characteristics. Especially used in natural marble crushed material bonding molding, products with good surface brightness, high hardness.
orthophthalic
400-600
4-6
orthophthalic unsaturated polyester resin has relatively high elongation at break and impact strength. It is suitable for being added to other resins, as it can enhance flexibility and impact strength. Its flexural fatigue resistance is better than that of Resin 228, making it suitable for being used alone to produce furniture carving products..
orthophthalic
700-950
3-5
70
70
3.7
10.0
good toughness, high hardness, good sanding, the product surface is flat without pinholes, suitable for piano and other high-grade wood paint.
orthophthalic
300-600
3-8
high elongation and impact strength. Suitable for adding other resins to increase flexibility and impact strength.
orthophthalic
400-600
3-5
orthophthalic unsaturated polyester resin low thermal expansion force during curing, making it suitable for casting in steel molds without cracking. It is used to manufacture bowling ball cores.
orthophthalic
550-650
4-6
with a Shore D hardness of 78 or higher. It is suitable for manufacturing the outer layer of bowling balls and can also be used in combination with 292N.
Phthalate
400-800
3-5
55
50
4.0
6.5
General transparent craft resin.
Phthalate
350-600
3-5
65
60
2.0
7.0
Good resistance to yellowing, high transparency, used for transparent crystal crafts.
Phthalate
350-600
3-5
65
60
2.0
7.0
Good resistance to yellowing, high transparency, used for making transparent flat panel crafts.
Double ring
120-220
9-14
20
15
The product has outstanding high-temperature performance at 200℃. It is easy to sand and easy to apply, making it suitable for use as a putty for powder coating on entire vehicles.
Specialty materials
150-300
9-14
22
17
Easy to sand, easy to apply, good high-temperature resistance, suitable for use as body putty.
Special modification
150-300
9-14
30
20
Good toughness, easy to polish, easy to apply and scrape, with good high-temperature resistance, suitable for making putty for the whole vehicle.
orthophthalic
600~800
5~7
60
60
10.0
12.0
With medium viscosity and medium reactivity, good toughness, excellent mechanical strength, good adhesive properties, good wetting properties and other characteristics. Especially used in natural marble crushed material bonding molding, products with good surface luminosity, good hardness.
orthophthalic
600~800
5~7
58
60
8.0
10.0
orthophthalic Styrene-free unsaturated polyester resin With medium viscosity and medium reactivity, good toughness, excellent mechanical strength, good bonding properties, good wetting properties and other characteristics. It is especially used for bonding and molding of natural marble crushed materials, with good surface brightness and good hardness.
Polyurethane modification
400-600
8-12
35
20
100
110
Polyurethane-modified resin features high elongation, excellent flexibility, and relatively high strength. It can be added to other resins to enhance their fracture resistance, elongation at break, and impact performance. Additionally, it can be used alone to produce impact-resistant products and flexible products..
Phthalate
500-600
20-30
55
45
15
20
Moderate hardness, excellent impact resistance, suitable for billiards.
Double ring
150-350
2-6
70
55
4.0
7.0
Medium viscosity and medium reactivity, fast curing after setting, crack-resistant, good toughness, suitable for basin casting, resin-based concrete casting and other products.
Orthophthalic
200-300
70-110
90
65
2.5
8.5
Orthophthalic Pre-Promoted Unsaturated Polyester Resin for Anchoring Agents This product features high reactivity, short gel time, fast curing speed, high strength, and a long storage life. It is suitable for use as a resin in slow-curing anchoring agents...
Note: If you need a detailed product manual or other information, please contact us.
Shanghai Xintianhe Resin Co., Ltd.
Address: Room 502, Building 23, Science and Technology Oasis, 1999 Yishan Road, Minhang District, Shanghai
National unified hotline: 400-820-9698
Telephone: 86-21-57485068 / +86 13917508287 (Sales Department)
E-mail: service@chinaresins.com
Concerned about the public.
day and resin